 题目:Microstructure and mechanical properties of TiB and Ti-6Al-4V composites by
        powder-metallurgy

   作者Yongren Liang, Qingwen Duan, Tuanwei Yang, Yinjiang Wu
   摘要TiB-reinforced Ti-6Al-4V composites were fabricated by powder metallurgical processes
         from Ti, TiB2 and Al-V powders. The powders were mechanically blended in a high energy
         ball mill. The powder obtained was pressed into billets and sintered in vacuum
         atmosphere, then forging and other hot treatments were applied to improve the
         dispersion and size of TiB particles. SEM was used to study the influences of TiB
         particles in the composites on microstructure. Because of the formation of ultrafine
         and stable TiB reinforcements, the TiB reinforced Ti-6Al-4V composites are found to
         exhibit excellent mechanical properties at room temperature.
   关键词titanium matrix composites(TMC), TiB, microstructure, mechanical properties
   发表期刊Proceedings of the 12th world conference on titanium 1523-1526
 
     
 
 题目:点阵结构金属多孔材料制造技术
   作者梁永仁; 吴引江; 周济; 曹柏亮; 杨团委; 刘高建; 李荣
   摘要本文综述了点阵结构金属多孔材料的主要拓扑形态及其制造技术,并对目前广泛采用的变形成型法、金属丝
         编织法,以及随后发展起来的快速成型和注射成型等技术进行了对比分析。最后,对点阵结构金属多孔材料
         研究的努力方向提出了一点建议。
   关键词点阵材料; 泡沫材料; 成型方法; 制造工艺
   发表期刊金属功能材料 , Metallic Functional Materials, 2012年01期
 
     
 
 题目:关于多孔材料过滤精度的探讨
   作者佘勃强; 董领锋; 吴引江; 周济; 王翠翠;
   摘要从多孔材料过滤精度的定义出发,探讨了过滤精度的评定方法和过滤精度与冒泡孔径间的关系,指出了过滤
         精度与冒泡孔径间具有一定的数值换算关系及换算注意事项,同时也指出了在过滤器设计使用和滤材选用时
         要考虑过滤精度评定时的试验条件、要结合工况条件对滤材标定过滤精度值进行修正。
   关键词多孔材料; 过滤精度; 多次通过法; 冒泡孔径;
   发表期刊过滤与分离 , Journal of Filtration & Separation, 2013年02期
 
     
 
 题目:考虑齿间摩擦力的齿根弯曲应力计算
   作者佘勃强; 吴引江; 崔亚辉
   摘要按照现行齿轮强度计算方法,全面地分析计算了齿间摩擦力对增速和减速传动中大、小轮齿根弯曲应力的影
         响。结果表明:考虑齿间摩擦力的影响后,从动轮的齿根应力有所减小,主动轮的齿根应力有所增加,特别是
         增速传动中的主动大齿轮较多,在设计时应予以考虑。
   关键词齿根弯曲应力; 齿间摩擦力; 主动轮; 从动轮;
   发表期刊装备制造技术 , Equipment Manufacturing Technology, 2013年06期
 
     
 
 题目:不锈钢粉末与丝网烧结多孔材料高温硫化性能研究
   作者南海娟; 吴引江; 张晓晗
   摘要为了考察滤材结构和形貌对材料抗高温硫化性能影响,研究了不锈钢316L、310S粉末与丝网烧结多孔材料在
         高温硫化氢气氛[350℃,介质:CO2+H2S(0.02%,体积分数)]中的硫化性能以及材料孔结构的稳定性,并利用
         光学显微镜观察表面形貌,从而评价耐蚀性能。结果表明:经过1 500h试验,316L、310S粉末烧结金属多孔
         材料在高温硫化氢气氛中耐腐蚀性能明显低于同类丝网材料,粉末与丝网烧结金属多孔材料的耐蚀性能差异
         主要由滤材结构和其比表面积决定。
   关键词粉末烧结; 丝网烧结; 高温硫化腐蚀; 比表面积;
   发表期刊粉末冶金技术 , Powder Metallurgy Technology, 2013年03期
 
     
 
 题目:Fabrication of porous sailon using Fe2O3 as pore former
   作者Qingwen Duan,Rongzhen Liu
   摘要Porous SiAlON ceramics were fabricated by carbothermal reduction niridation method
         using Fe2O3 as pore former. Particle size effects of Fe2O3 were reported in this paper.
         The results showed that composites were composed by SiAlON , AlN and Fe2O3 phases. The
         median pore diameter of Sialon was affected by the composition and particle size of
         Fe2O3. The fracture mode of this material was intergranular. With the increasing of
         Fe2O3 additions, the porosity of this materials increased. The bending strength of this
         material was reversely propotional to Fe2O3 particle size. The maximum bending strength
         of Porous matirials with 30wt.% Fe2O3 additions (with a porosity about 65% and the pore
         size is about 1μm) could reach 22 MPa. The porous Sialon ceramics with a smaller pore
         size exhibits a higher bending strength.
 
     
 
 题目:煤气化锁斗高压过滤器滤芯断裂原因及改进措施
   作者佘勃强; 吴引江; 王翠翠; 周济
   摘要为了减少和避免煤气化锁斗高压过滤器滤芯的断裂,降低设备故障率,提高煤气化装置的开车率和保证其长
         周期稳定运行,研究了多个项目现场中的滤芯断裂状况。结果表明:滤芯的断裂状况大都相似,断裂部位大都
         在滤芯根部且往往伴随有滤芯管体的弯曲。综合分析了滤芯断裂的原因,提出了相应的改进措施和注意事项
   关键词煤气化; 锁斗高压过滤器; 滤芯断裂; 改进
   发表期刊洁净煤技术 , Clean Coal Technology, 2014年01期
 
     
 
 题目:高温气体除尘用金属过滤器研发进展
   作者南海娟,吴引江
   摘要在现代工业生产过程中,涉及含尘气体在高温下直接净化除尘的领域十分广泛,烧结金属过滤器为高温除尘
         提供了一种高效、高强、长寿命、低成本过滤方案。金属过滤介质对高温复杂气氛工况的耐受性还在进一
         步研究中。过滤器工作环境影响其使用寿命和工作效率,过滤器应该在设计参数范围内工作,以避免工艺
         参数波动造成过滤材料不能发挥其最大效力。过滤器在反吹系统设计上也要与过滤材料过滤性能、机械性
         能相匹配,比如反吹频率、反吹时间、反吹压力等与金属过滤材料抗压阻能力、金属过滤材料再生能力相
         匹配。
   关键词煤气化; 锁斗高压过滤器; 滤芯断裂; 改进
   发表期刊第四届脱硫脱硝除尘行业关键技术研讨会论文集
 
     
 
 
 
 
 

 
   
     